Poinot Delphine - One of the best experts on this subject based on the ideXlab platform.
-
Etude de couches minces de CuO pour électrode positive à forte capacité surfacique : Application aux microbatteries au lithium
HAL CCSD, 2011Co-Authors: Poinot DelphineAbstract:The miniaturization of electronic components and their increasing number of functionalities induce a great interest for energy Microsources such as thin films batteries. There are mainly developed for secondary systems, even if primary systems are also convenient for some applications. Currently, the main limitation is their specific capacity which does not exceed 200 µAh.cm 2.µm 1. In order to get a system having a high surfacic capacity, we focused on CuO, which react with lithium according to a conversion mechanism and exhibit a large theoretical capacity (425 µAh .cm-2.µm-1). CuO thin films were prepared by radiofrequency magnetron sputtering in a reactive mixture (Ar + O2). The influence of some deposition parameters (oxygen concentration, total pressure, substrate-target distance, the intentional heating or not of the substrates, target configuration) on their chemical, morphological and structural properties were investigated. The latter were also linked to their electrochemical performances, obtained with a liquid electrolyte or a solid electrolyte.La miniaturisation des appareils électroniques et la multiplication de leur fonctionnalités explique l'intérêt croissant porté aux Microsources d'énergie telles que les microbatteries au lithium. Ces dernières sont principalement conçues pour une utilisation rechargeable, mais des systèmes non rechargeables peuvent également êtes envisagés pour certaines applications. Actuellement, la principale limitation de ces systèmes est leur capacité surfacique, n'excédant pas 200 µAh.cm-2. Afin d'obtenir une forte capacité surfacique, nous nous sommes intéressés à CuO, un matériau réagissant avec le lithium suivant un mécanisme de conversion, et présentant une capacité volumique théorique élevée (425 µAh .cm-2.µm-1). Des couches minces de CuO ont ainsi été préparées par pulvérisation radiofréquence à cathode magnétron sous atmosphère réactive (Ar + O2). L'influence des paramètres de dépôts (concentration d'oxygène, pression totale, température des substrats, distance cible-substrat, configuration de la cible) sur leurs propriétés chimiques, morphologiques et structurales a été étudiée. Ces dernières ont également été corrélées à leurs performances électrochimiques, obtenues avec un électrolyte liquide ou un électrolyte solide
-
Etude de couches minces de CuO pour électrode positive à forte capacité surfacique (Application aux microbatteries au lithium)
2011Co-Authors: Poinot Delphine, Pecquenard Brigitte, Le Cras FrédéricAbstract:La miniaturisation des appareils électroniques et la multiplication de leur fonctionnalités explique l intérêt croissant porté aux Microsources d énergie telles que les microbatteries au lithium. Ces dernières sont principalement conçues pour une utilisation rechargeable, mais des systèmes non rechargeables peuvent également êtes envisagés pour certaines applications. Actuellement, la principale limitation de ces systèmes est leur capacité surfacique, n excédant pas 200 Ah.cm-2. Afin d obtenir une forte capacité surfacique, nous nous sommes intéressés à CuO, un matériau réagissant avec le lithium suivant un mécanisme de conversion, et présentant une capacité volumique théorique élevée (425 Ah .cm-2. m-1). Des couches minces de CuO ont ainsi été préparées par pulvérisation radiofréquence à cathode magnétron sous atmosphère réactive (Ar + O2). L influence des paramètres de dépôts (concentration d oxygène, pression totale, température des substrats, distance cible-substrat, configuration de la cible) sur leurs propriétés chimiques, morphologiques et structurales a été étudiée. Ces dernières ont également été corrélées à leurs performances électrochimiques, obtenues avec un électrolyte liquide ou un électrolyte solide.The miniaturization of electronic components and their increasing number of functionalities induce a great interest for energy Microsources such as thin films batteries. There are mainly developed for secondary systems, even if primary systems are also convenient for some applications. Currently, the main limitation is their specific capacity which does not exceed 200 Ah.cm 2. m 1. In order to get a system having a high surfacic capacity, we focused on CuO, which react with lithium according to a conversion mechanism and exhibit a large theoretical capacity (425 Ah .cm-2. m-1). CuO thin films were prepared by radiofrequency magnetron sputtering in a reactive mixture (Ar + O2). The influence of some deposition parameters (oxygen concentration, total pressure, substrate-target distance, the intentional heating or not of the substrates, target configuration) on their chemical, morphological and structural properties were investigated. The latter were also linked to their electrochemical performances, obtained with a liquid electrolyte or a solid electrolyte.BORDEAUX1-Bib.electronique (335229901) / SudocSudocFranceF
-
Study of CuO thin film for high-capacity positive electrode surface : Application to lithium microbatteries
2011Co-Authors: Poinot DelphineAbstract:La miniaturisation des appareils électroniques et la multiplication de leur fonctionnalités explique l’intérêt croissant porté aux Microsources d’énergie telles que les microbatteries au lithium. Ces dernières sont principalement conçues pour une utilisation rechargeable, mais des systèmes non rechargeables peuvent également êtes envisagés pour certaines applications. Actuellement, la principale limitation de ces systèmes est leur capacité surfacique, n’excédant pas 200 µAh.cm-2. Afin d’obtenir une forte capacité surfacique, nous nous sommes intéressés à CuO, un matériau réagissant avec le lithium suivant un mécanisme de conversion, et présentant une capacité volumique théorique élevée (425 µAh .cm-2.µm-1). Des couches minces de CuO ont ainsi été préparées par pulvérisation radiofréquence à cathode magnétron sous atmosphère réactive (Ar + O2). L’influence des paramètres de dépôts (concentration d’oxygène, pression totale, température des substrats, distance cible-substrat, configuration de la cible) sur leurs propriétés chimiques, morphologiques et structurales a été étudiée. Ces dernières ont également été corrélées à leurs performances électrochimiques, obtenues avec un électrolyte liquide ou un électrolyte solide.The miniaturization of electronic components and their increasing number of functionalities induce a great interest for energy Microsources such as thin films batteries. There are mainly developed for secondary systems, even if primary systems are also convenient for some applications. Currently, the main limitation is their specific capacity which does not exceed 200 µAh.cm 2.µm 1. In order to get a system having a high surfacic capacity, we focused on CuO, which react with lithium according to a conversion mechanism and exhibit a large theoretical capacity (425 µAh .cm-2.µm-1). CuO thin films were prepared by radiofrequency magnetron sputtering in a reactive mixture (Ar + O2). The influence of some deposition parameters (oxygen concentration, total pressure, substrate-target distance, the intentional heating or not of the substrates, target configuration) on their chemical, morphological and structural properties were investigated. The latter were also linked to their electrochemical performances, obtained with a liquid electrolyte or a solid electrolyte
Trupkovic Alexandra - One of the best experts on this subject based on the ideXlab platform.
-
Study of lithium borates glasses usable in microbatteries : correlation between ionic conductivity and thermomecanical properties
2009Co-Authors: Trupkovic AlexandraAbstract:L’utilisation croissante de systèmes électroniques miniaturisés induit une forte demande en Microsources d’énergie performantes, telles que les microbatteries au lithium. En vue d’améliorer les propriétés de l’électrolyte, nous avons étudié les propriétés électriques et thermomécaniques d’électrolytes solides de type borate de lithium. Une corrélation entre la conductivité ionique et le coefficient de dilatation thermique (CTE) a été mise en évidence pour différentes compositions de verres massifs. A partir des résultats de CTE obtenus, un modèle de prédiction basé sur les travaux de Appen permettant la détermination de ce dernier en fonction de la composition chimique a été développé. Dans un second temps, différentes techniques de préparation de cibles denses nitrurées ont été mises en œuvre afin d’abaisser le CTE de la cible et ainsi permettre son utilisation sur une plus longue durée. Par ailleurs, l’utilisation d’une cible nitrurée a également été envisagée pour augmenter la teneur en azote dans les couches minces. Finalement, des couches minces d’électrolyte de différentes compositions ont été préparées par pulvérisation cathodique (sous plasma d’argon ou d’azote pur) et ont fait l’objet d’une caractérisation chimique, structurale, électrique et thermomécanique. Le rôle bénéfique de l’azote sur la conductivité ionique des couches minces a ainsi pu être confirmé.The growing use of miniaturized electronic devices results in a strong demand in high-performance energy Microsources, such as lithium microbatteries. In order to improve electrolyte properties, we have studied the electrical and thermomechanical properties of bulk electrolyte based on lithium borate glasses. A correlation between ionic conductivity and thermal expansion coefficient has been evidenced for bulk materials. Further to CTE results, a predicting model based on studies leaded by Appen allowing a determination of CTE as a function of the chemical composition has been developed. In a second time, different preparation techniques of dense nitrated targets have been implemented in order to decrease their CTE and to allow their use for a longer period. Otherwise, nitrated targets have also been considered to increase the nitrogen content in thin films. Finally, electrolyte thin films of different compositions have been prepared by rf magnetron sputtering (under pure argon or nitrogen gas) and have been chemically, structurally, electrically and thermomecanically characterized. The favorable influence of nitrogen on the ionic conductivity of thin films has been confirmed
-
Etude de verres borates de lithium utilisables dans les microbatteries : corrélation conductivité ionique / propriétés thermomécaniques
HAL CCSD, 2009Co-Authors: Trupkovic AlexandraAbstract:The growing use of miniaturized electronic devices results in a strong demand in high-performance energy Microsources, such as lithium microbatteries. In order to improve electrolyte properties, we have studied the electrical and thermomechanical properties of bulk electrolyte based on lithium borate glasses. A correlation between ionic conductivity and thermal expansion coefficient has been evidenced for bulk materials. Further to CTE results, a predicting model based on studies leaded by Appen allowing a determination of CTE as a function of the chemical composition has been developed. In a second time, different preparation techniques of dense nitrated targets have been implemented in order to decrease their CTE and to allow their use for a longer period. Otherwise, nitrated targets have also been considered to increase the nitrogen content in thin films. Finally, electrolyte thin films of different compositions have been prepared by rf magnetron sputtering (under pure argon or nitrogen gas) and have been chemically, structurally, electrically and thermomecanically characterized. The favorable influence of nitrogen on the ionic conductivity of thin films has been confirmed.L'utilisation croissante de systèmes électroniques miniaturisés induit une forte demande en Microsources d'énergie performantes, telles que les microbatteries au lithium. En vue d'améliorer les propriétés de l'électrolyte, nous avons étudié les propriétés électriques et thermomécaniques d'électrolytes solides de type borate de lithium. Une corrélation entre la conductivité ionique et le coefficient de dilatation thermique (CTE) a été mise en évidence pour différentes compositions de verres massifs. A partir des résultats de CTE obtenus, un modèle de prédiction basé sur les travaux de Appen permettant la détermination de ce dernier en fonction de la composition chimique a été développé. Dans un second temps, différentes techniques de préparation de cibles denses nitrurées ont été mises en œuvre afin d'abaisser le CTE de la cible et ainsi permettre son utilisation sur une plus longue durée. Par ailleurs, l'utilisation d'une cible nitrurée a également été envisagée pour augmenter la teneur en azote dans les couches minces. Finalement, des couches minces d'électrolyte de différentes compositions ont été préparées par pulvérisation cathodique (sous plasma d'argon ou d'azote pur) et ont fait l'objet d'une caractérisation chimique, structurale, électrique et thermomécanique. Le rôle bénéfique de l'azote sur la conductivité ionique des couches minces a ainsi pu être confirmé
-
Etude de verres borates de lithium utilisables dans les microbatteries (corrélation conductivité ionique / propriétés thermomécaniques)
2009Co-Authors: Trupkovic Alexandra, Levasseur Alain, Pecquenard BrigitteAbstract:L utilisation croissante de systèmes électroniques miniaturisés induit une forte demande en Microsources d énergie performantes, telles que les microbatteries au lithium. En vue d améliorer les propriétés de l électrolyte, nous avons étudié les propriétés électriques et thermomécaniques d électrolytes solides de type borate de lithium. Une corrélation entre la conductivité ionique et le coefficient de dilatation thermique (CTE) a été mise en évidence pour différentes compositions de verres massifs. A partir des résultats de CTE obtenus, un modèle de prédiction basé sur les travaux de Appen permettant la détermination de ce dernier en fonction de la composition chimique a été développé. Dans un second temps, différentes techniques de préparation de cibles denses nitrurées ont été mises en œuvre afin d abaisser le CTE de la cible et ainsi permettre son utilisation sur une plus longue durée. Par ailleurs, l utilisation d une cible nitrurée a également été envisagée pour augmenter la teneur en azote dans les couches minces. Finalement, des couches minces d électrolyte de différentes compositions ont été préparées par pulvérisation cathodique (sous plasma d argon ou d azote pur) et ont fait l objet d une caractérisation chimique, structurale, électrique et thermomécanique. Le rôle bénéfique de l azote sur la conductivité ionique des couches minces a ainsi pu être confirmé.The growing use of miniaturized electronic devices results in a strong demand in high-performance energy Microsources, such as lithium microbatteries. In order to improve electrolyte properties, we have studied the electrical and thermomechanical properties of bulk electrolyte based on lithium borate glasses. A correlation between ionic conductivity and thermal expansion coefficient has been evidenced for bulk materials. Further to CTE results, a predicting model based on studies leaded by Appen allowing a determination of CTE as a function of the chemical composition has been developed. In a second time, different preparation techniques of dense nitrated targets have been implemented in order to decrease their CTE and to allow their use for a longer period. Otherwise, nitrated targets have also been considered to increase the nitrogen content in thin films. Finally, electrolyte thin films of different compositions have been prepared by rf magnetron sputtering (under pure argon or nitrogen gas) and have been chemically, structurally, electrically and thermomecanically characterized. The favorable influence of nitrogen on the ionic conductivity of thin films has been confirmed.BORDEAUX1-Bib.electronique (335229901) / SudocSudocFranceF
Candela Yves - One of the best experts on this subject based on the ideXlab platform.
-
Microcavités de silice (excitation par fibre des modes de galerie et fonctionnalisation par des nanocristaux de silicium)
2011Co-Authors: Candela Yves, Hare JeanAbstract:As a first step, this manuscript gives theoretical descriptions of silica microsphere and microtoroid modes. Then, their fabrication is presented. Some improvements, such as the production of sub-20 m diameter spheres and the use of circular polarization to improve the symmetry of the toroid, are described. We present an in-depth study of their excitation by the taper coupler. We put the stress on the evanescent wave interference phenomenon occurring in the gap. This is responsible for resonance broadening and shifts I study theoretically and experimentally. The previous approach leads to a very powerful technique to determine the radial order. We observe also unexpected resonance lineshapes resulting in coupler modes interferences by analogy with a Mach-Zehnder interferometer. Finally, we raise the issue of Silicon nanocrystal (Si-nc) based microsource using these resonators. The emitters have a controlled size ranging from 0.6 to 6 nm. The CO2 laser reflow activates the Si-nc photoluminescence around 750 nm, but leads to coalescence of the material and a partial destruction. The optical filling factor and the defects in the matrix seem to be the main limitations for significant improvement of the performances. It has been possible to collect the emission from Si-nc coupled with microtoroids in the near and far fields.Cette thèse exploite les modes de galerie de microcavités optiques, qui résultent d un guidage par réflexion totale interne et possèdent des facteurs de qualité très élevés et de faibles volumes modaux. Ce mémoire rappelle dans un premier temps la description théorique des modes des microsphères et des microtores de silice. Leur fabrication est ensuite présentée, en soulignant les améliorations apportées au cours de la thèse, notamment la production de sphères de diamètre inférieur à 20 m, et l amélioration de la symétrie des tores à l aide d une polarisation circulaire. Nous présentons une étude détaillée de leur excitation par un coupleur fibré en insistant sur le phénomène d interférence en ondes évanescentes qui se produit dans le gap. Ce phénomène est responsable des élargissements et déplacements des résonances dont je présente une étude poussée. Cette approche débouche sur une méthode très efficace de détermination de l ordre radial. Par ailleurs, on observe des formes de résonance inattendues, qui résultent d interférences entre deux modes du coupleur dans une configuration analogue à l interféromètre de Mach-Zehnder. Nous abordons enfin la réalisation de Microsources fondées sur l émission de nanocristaux de silicium (NC Si) dans ces cavités. Les émetteurs ont des tailles contrôlées allant de 0,6 à 6 nm. Le chauffage au laser CO2 active la photoluminescence des NC Si autour de 750 nm, puis induit leur destruction partielle par coalescence. Le facteur de remplissage optique et les défauts de la matrice apparaissent comme les principaux obstacles à une amélioration significative des performances. Il a été possible de collecter l émission de NC Si couplés à des microtores, en champs proche et lointain.PARIS-BIUSJ-Biologie recherche (751052107) / SudocSudocFranceF
-
Microcavités de silice : Excitation par fibre des modes de galerie et fonctionnalisation par des nanocristaux de silicium
HAL CCSD, 2011Co-Authors: Candela YvesAbstract:This thesis uses whispering gallery modes of optical microcavities. They result from total internal reflexion guidance and exibit very high quality factor and small mode volume. As a first step, this manuscript gives theoretical descriptions of silica microsphere and microtoroid modes. Then, their fabrication is presented. Some improvements, such as the production of sub-20 μm diameter spheres and the use of circular polarization to improve the symmetry of the toroid, are described. We present an in-depth study of their excitation by the taper coupler. We put the stress on the evanescent wave interference phenomenon occurring in the gap. This is responsible for resonance broadening and shifts I study theoretically and experimentally. The previous approach leads to a very powerful technique to determine the radial order. We observe also unexpected resonance lineshapes resulting in coupler modes interferences by analogy with a Mach-Zehnder interferometer. Finally, we raise the issue of Silicon nanocrystal (Si-nc) based microsource using these resonators. The emitters have a controlled size ranging from 0.6 to 6 nm. The CO2 laser reflow activates the Si-nc photoluminescence around 750 nm, but leads to coalescence of the material and a partial destruction. The optical filling factor and the defects in the matrix seem to be the main limitations for significant improvement of the performances. It has been possible to collect the emission from Si-nc coupled with microtoroids in the near and far fields.Cette thèse exploite les modes de galerie de microcavités optiques, qui résultent d'un guidage par réflexion totale interne et possèdent des facteurs de qualité très élevés et de faibles volumes modaux. Ce mémoire rappelle dans un premier temps la description théorique des modes des microsphères et des microtores de silice. Leur fabrication est ensuite présentée, en soulignant les améliorations apportées au cours de la thèse, notamment la production de sphères de diamètre inférieur à 20 μm, et l'amélioration de la symétrie des tores à l'aide d'une polarisation circulaire. Nous présentons une étude détaillée de leur excitation par un coupleur fibré en insistant sur le phénomène d'interférence en ondes évanescentes qui se produit dans le gap. Ce phénomène est responsable des élargissements et déplacements des résonances dont je présente une étude poussée. Cette approche débouche sur une méthode très efficace de détermination de l'ordre radial. Par ailleurs, on observe des formes de résonance inattendues, qui résultent d'interférences entre deux modes du coupleur dans une configuration analogue à l'interféromètre de Mach-Zehnder. Nous abordons enfin la réalisation de Microsources fondées sur l'émission de nanocristaux de silicium (NC Si) dans ces cavités. Les émetteurs ont des tailles contrôlées allant de 0,6 à 6 nm. Le chauffage au laser CO2 active la photoluminescence des NC Si autour de 750 nm, puis induit leur destruction partielle par coalescence. Le facteur de remplissage optique et les défauts de la matrice apparaissent comme les principaux obstacles à une amélioration significative des performances. Il a été possible de collecter l'émission de NC Si couplés à des microtores, en champs proche et lointain
Pecquenard Brigitte - One of the best experts on this subject based on the ideXlab platform.
-
Etude de couches minces de CuO pour électrode positive à forte capacité surfacique (Application aux microbatteries au lithium)
2011Co-Authors: Poinot Delphine, Pecquenard Brigitte, Le Cras FrédéricAbstract:La miniaturisation des appareils électroniques et la multiplication de leur fonctionnalités explique l intérêt croissant porté aux Microsources d énergie telles que les microbatteries au lithium. Ces dernières sont principalement conçues pour une utilisation rechargeable, mais des systèmes non rechargeables peuvent également êtes envisagés pour certaines applications. Actuellement, la principale limitation de ces systèmes est leur capacité surfacique, n excédant pas 200 Ah.cm-2. Afin d obtenir une forte capacité surfacique, nous nous sommes intéressés à CuO, un matériau réagissant avec le lithium suivant un mécanisme de conversion, et présentant une capacité volumique théorique élevée (425 Ah .cm-2. m-1). Des couches minces de CuO ont ainsi été préparées par pulvérisation radiofréquence à cathode magnétron sous atmosphère réactive (Ar + O2). L influence des paramètres de dépôts (concentration d oxygène, pression totale, température des substrats, distance cible-substrat, configuration de la cible) sur leurs propriétés chimiques, morphologiques et structurales a été étudiée. Ces dernières ont également été corrélées à leurs performances électrochimiques, obtenues avec un électrolyte liquide ou un électrolyte solide.The miniaturization of electronic components and their increasing number of functionalities induce a great interest for energy Microsources such as thin films batteries. There are mainly developed for secondary systems, even if primary systems are also convenient for some applications. Currently, the main limitation is their specific capacity which does not exceed 200 Ah.cm 2. m 1. In order to get a system having a high surfacic capacity, we focused on CuO, which react with lithium according to a conversion mechanism and exhibit a large theoretical capacity (425 Ah .cm-2. m-1). CuO thin films were prepared by radiofrequency magnetron sputtering in a reactive mixture (Ar + O2). The influence of some deposition parameters (oxygen concentration, total pressure, substrate-target distance, the intentional heating or not of the substrates, target configuration) on their chemical, morphological and structural properties were investigated. The latter were also linked to their electrochemical performances, obtained with a liquid electrolyte or a solid electrolyte.BORDEAUX1-Bib.electronique (335229901) / SudocSudocFranceF
-
Etude de verres borates de lithium utilisables dans les microbatteries (corrélation conductivité ionique / propriétés thermomécaniques)
2009Co-Authors: Trupkovic Alexandra, Levasseur Alain, Pecquenard BrigitteAbstract:L utilisation croissante de systèmes électroniques miniaturisés induit une forte demande en Microsources d énergie performantes, telles que les microbatteries au lithium. En vue d améliorer les propriétés de l électrolyte, nous avons étudié les propriétés électriques et thermomécaniques d électrolytes solides de type borate de lithium. Une corrélation entre la conductivité ionique et le coefficient de dilatation thermique (CTE) a été mise en évidence pour différentes compositions de verres massifs. A partir des résultats de CTE obtenus, un modèle de prédiction basé sur les travaux de Appen permettant la détermination de ce dernier en fonction de la composition chimique a été développé. Dans un second temps, différentes techniques de préparation de cibles denses nitrurées ont été mises en œuvre afin d abaisser le CTE de la cible et ainsi permettre son utilisation sur une plus longue durée. Par ailleurs, l utilisation d une cible nitrurée a également été envisagée pour augmenter la teneur en azote dans les couches minces. Finalement, des couches minces d électrolyte de différentes compositions ont été préparées par pulvérisation cathodique (sous plasma d argon ou d azote pur) et ont fait l objet d une caractérisation chimique, structurale, électrique et thermomécanique. Le rôle bénéfique de l azote sur la conductivité ionique des couches minces a ainsi pu être confirmé.The growing use of miniaturized electronic devices results in a strong demand in high-performance energy Microsources, such as lithium microbatteries. In order to improve electrolyte properties, we have studied the electrical and thermomechanical properties of bulk electrolyte based on lithium borate glasses. A correlation between ionic conductivity and thermal expansion coefficient has been evidenced for bulk materials. Further to CTE results, a predicting model based on studies leaded by Appen allowing a determination of CTE as a function of the chemical composition has been developed. In a second time, different preparation techniques of dense nitrated targets have been implemented in order to decrease their CTE and to allow their use for a longer period. Otherwise, nitrated targets have also been considered to increase the nitrogen content in thin films. Finally, electrolyte thin films of different compositions have been prepared by rf magnetron sputtering (under pure argon or nitrogen gas) and have been chemically, structurally, electrically and thermomecanically characterized. The favorable influence of nitrogen on the ionic conductivity of thin films has been confirmed.BORDEAUX1-Bib.electronique (335229901) / SudocSudocFranceF
Le Cras Frédéric - One of the best experts on this subject based on the ideXlab platform.
-
Etude de couches minces de CuO pour électrode positive à forte capacité surfacique (Application aux microbatteries au lithium)
2011Co-Authors: Poinot Delphine, Pecquenard Brigitte, Le Cras FrédéricAbstract:La miniaturisation des appareils électroniques et la multiplication de leur fonctionnalités explique l intérêt croissant porté aux Microsources d énergie telles que les microbatteries au lithium. Ces dernières sont principalement conçues pour une utilisation rechargeable, mais des systèmes non rechargeables peuvent également êtes envisagés pour certaines applications. Actuellement, la principale limitation de ces systèmes est leur capacité surfacique, n excédant pas 200 Ah.cm-2. Afin d obtenir une forte capacité surfacique, nous nous sommes intéressés à CuO, un matériau réagissant avec le lithium suivant un mécanisme de conversion, et présentant une capacité volumique théorique élevée (425 Ah .cm-2. m-1). Des couches minces de CuO ont ainsi été préparées par pulvérisation radiofréquence à cathode magnétron sous atmosphère réactive (Ar + O2). L influence des paramètres de dépôts (concentration d oxygène, pression totale, température des substrats, distance cible-substrat, configuration de la cible) sur leurs propriétés chimiques, morphologiques et structurales a été étudiée. Ces dernières ont également été corrélées à leurs performances électrochimiques, obtenues avec un électrolyte liquide ou un électrolyte solide.The miniaturization of electronic components and their increasing number of functionalities induce a great interest for energy Microsources such as thin films batteries. There are mainly developed for secondary systems, even if primary systems are also convenient for some applications. Currently, the main limitation is their specific capacity which does not exceed 200 Ah.cm 2. m 1. In order to get a system having a high surfacic capacity, we focused on CuO, which react with lithium according to a conversion mechanism and exhibit a large theoretical capacity (425 Ah .cm-2. m-1). CuO thin films were prepared by radiofrequency magnetron sputtering in a reactive mixture (Ar + O2). The influence of some deposition parameters (oxygen concentration, total pressure, substrate-target distance, the intentional heating or not of the substrates, target configuration) on their chemical, morphological and structural properties were investigated. The latter were also linked to their electrochemical performances, obtained with a liquid electrolyte or a solid electrolyte.BORDEAUX1-Bib.electronique (335229901) / SudocSudocFranceF