David C Dunand - One of the best experts on this subject based on the ideXlab platform.

  • microstructure and porosity evolution during Sintering of ni mn ga wires printed from inks containing elemental powders
    Intermetallics, 2019
    Co-Authors: Shannon L. Taylor, Ramille N Shah, David C Dunand
    Abstract:

    Abstract Ni-29Mn-21.5Ga (at. %) wires are fabricated via a combination of (i) extrusion of liquid inks containing a binder, solvents, and elemental Ni, Mn, and Ga powders and (ii) heat treatments to remove the polymer binder and to interdiffuse and sinter the powders. To study the microstructural evolution, Sintering mechanisms, and grain growth in these wires, both ex situ metallography and in situ X-Ray tomography were conducted while Sintering at 800–1050 °C for up to 4 h. After debinding, Ga-rich regions melt and induce Transient liquid phase Sintering of the surrounding Ni and Mn powders, resulting in localized swelling of the wires and an increase in the wire porosity. After solidification of the melt and diffusion of the Ga into the Ni and Mn powders, solid-state Sintering occurs. The interdiffusion of Ni, Mn, and Ga during solid-state Sintering improves Sintering compared to fully pre-alloyed powders. At the end of the 4 h Sintering period, chemically homogenized, oligocrystalline wires with bamboo-like grains are observed with porosities ranging from 30 to 57%. Furthermore, significant grain growth occurs in wires sintered at 1000 and 1050 °C (11–35 μm vs. 1–10 μm initial powder size). The results from this study enable tailoring the porosity and grain size of printed Ni-Mn-Ga wires and 3D-printed micro-architectures and may be used to enhance their magnetic shape-memory and magnetocaloric effects in future work.

  • niti nb micro trusses fabricated via extrusion based 3d printing of powders and Transient liquid phase Sintering
    Acta Biomaterialia, 2018
    Co-Authors: Shannon L. Taylor, Amaka J. Ibeh, Adam E Jakus, Ramille N Shah, David C Dunand
    Abstract:

    Abstract We present a novel additive manufacturing method for NiTi-Nb micro-trusses combining (i) extrusion-based 3D-printing of liquid inks containing NiTi and Nb powders, solvents, and a polymer binder into micro-trusses with 0/90° ABAB layers of parallel, ∼600 µm struts spaced 1 mm apart and (ii) subsequent heat-treatment to remove the binder and solvents, and then bond the NiTi powders using liquid phase Sintering via the formation of a Transient NiTi-Nb eutectic phase. We investigate the effects of Nb concentration (0, 1.5, 3.1, 6.7 at.% Nb) on the porosity, microstructure, and phase transformations of the printed NiTi-Nb micro-trusses. Micro-trusses with the highest Nb content exhibit long channels (from 3D-printing) and struts with smaller interconnected porosity (from partial Sintering), resulting in overall porosities of ∼75% and low compressive stiffnesses of 1–1.6 GPa, similar to those of trabecular bone and in agreement with analytical and finite element modeling predictions. Diffusion of Nb into the NiTi particles from the bond regions results in a Ni-rich composition as the Nb replaces Ti atoms, leading to decreased martensite/austenite transformation temperatures. Adult human mesenchymal stem cells seeded on these micro-trusses showed excellent viability, proliferation, and extracellular matrix deposition over 14 days in culture. Statement of Significance Near-equiatomic NiTi micro-trusses are attractive for biomedical applications such as stents, actuators, and bone implants because of their combination of biocompatibility, low compressive stiffness, high surface area, and shape-memory or superelasticity. Extrusion-based 3D-printing of NiTi powder-based inks into micro-trusses is feasible, but the subsequent Sintering of the powders into dense struts is unachievable due to low diffusivity, large particle size, and low packing density of the NiTi powders. We present a solution, whereby Nb powders are added to the NiTi inks, thus forming during Sintering a eutectic NiTi-Nb liquid phase which bonds the solid NiTi powders and improves densification of the struts. This study investigates the microstructure, porosity, phase transformation behavior, compressive stiffness, and cytocompatibility of these printed NiTi-Nb micro-trusses.

  • niti nb micro trusses fabricated via extrusion based 3d printing of powders and Transient liquid phase Sintering
    Acta Biomaterialia, 2018
    Co-Authors: Shannon L. Taylor, Amaka J. Ibeh, Adam E Jakus, Ramille N Shah, David C Dunand
    Abstract:

    Abstract We present a novel additive manufacturing method for NiTi-Nb micro-trusses combining (i) extrusion-based 3D-printing of liquid inks containing NiTi and Nb powders, solvents, and a polymer binder into micro-trusses with 0/90° ABAB layers of parallel, ∼600 µm struts spaced 1 mm apart and (ii) subsequent heat-treatment to remove the binder and solvents, and then bond the NiTi powders using liquid phase Sintering via the formation of a Transient NiTi-Nb eutectic phase. We investigate the effects of Nb concentration (0, 1.5, 3.1, 6.7 at.% Nb) on the porosity, microstructure, and phase transformations of the printed NiTi-Nb micro-trusses. Micro-trusses with the highest Nb content exhibit long channels (from 3D-printing) and struts with smaller interconnected porosity (from partial Sintering), resulting in overall porosities of ∼75% and low compressive stiffnesses of 1–1.6 GPa, similar to those of trabecular bone and in agreement with analytical and finite element modeling predictions. Diffusion of Nb into the NiTi particles from the bond regions results in a Ni-rich composition as the Nb replaces Ti atoms, leading to decreased martensite/austenite transformation temperatures. Adult human mesenchymal stem cells seeded on these micro-trusses showed excellent viability, proliferation, and extracellular matrix deposition over 14 days in culture. Statement of Significance Near-equiatomic NiTi micro-trusses are attractive for biomedical applications such as stents, actuators, and bone implants because of their combination of biocompatibility, low compressive stiffness, high surface area, and shape-memory or superelasticity. Extrusion-based 3D-printing of NiTi powder-based inks into micro-trusses is feasible, but the subsequent Sintering of the powders into dense struts is unachievable due to low diffusivity, large particle size, and low packing density of the NiTi powders. We present a solution, whereby Nb powders are added to the NiTi inks, thus forming during Sintering a eutectic NiTi-Nb liquid phase which bonds the solid NiTi powders and improves densification of the struts. This study investigates the microstructure, porosity, phase transformation behavior, compressive stiffness, and cytocompatibility of these printed NiTi-Nb micro-trusses.

  • processing of niti foams by Transient liquid phase Sintering
    Journal of Materials Engineering and Performance, 2011
    Co-Authors: Ampika Bansiddhi, David C Dunand
    Abstract:

    Porous NiTi was produced by Sintering pre-alloyed NiTi powders (with small Ni addition to form Ni-rich composition) with NaCl powders which are removed to create 40-60 vol.% macropores which are open to the surface, blocky in shape, and 100-400 μm in size. The microporosity present between the NiTi powders is infiltrated by an in situ created NiTi-Nb eutectic liquid which, after solidification, densifies the NiTi powders into dense struts. This processing technique allows for separate control of the macroporous structure, and the densification and composition of the NiTi struts.

Shannon L. Taylor - One of the best experts on this subject based on the ideXlab platform.

  • microstructure and porosity evolution during Sintering of ni mn ga wires printed from inks containing elemental powders
    Intermetallics, 2019
    Co-Authors: Shannon L. Taylor, Ramille N Shah, David C Dunand
    Abstract:

    Abstract Ni-29Mn-21.5Ga (at. %) wires are fabricated via a combination of (i) extrusion of liquid inks containing a binder, solvents, and elemental Ni, Mn, and Ga powders and (ii) heat treatments to remove the polymer binder and to interdiffuse and sinter the powders. To study the microstructural evolution, Sintering mechanisms, and grain growth in these wires, both ex situ metallography and in situ X-Ray tomography were conducted while Sintering at 800–1050 °C for up to 4 h. After debinding, Ga-rich regions melt and induce Transient liquid phase Sintering of the surrounding Ni and Mn powders, resulting in localized swelling of the wires and an increase in the wire porosity. After solidification of the melt and diffusion of the Ga into the Ni and Mn powders, solid-state Sintering occurs. The interdiffusion of Ni, Mn, and Ga during solid-state Sintering improves Sintering compared to fully pre-alloyed powders. At the end of the 4 h Sintering period, chemically homogenized, oligocrystalline wires with bamboo-like grains are observed with porosities ranging from 30 to 57%. Furthermore, significant grain growth occurs in wires sintered at 1000 and 1050 °C (11–35 μm vs. 1–10 μm initial powder size). The results from this study enable tailoring the porosity and grain size of printed Ni-Mn-Ga wires and 3D-printed micro-architectures and may be used to enhance their magnetic shape-memory and magnetocaloric effects in future work.

  • niti nb micro trusses fabricated via extrusion based 3d printing of powders and Transient liquid phase Sintering
    Acta Biomaterialia, 2018
    Co-Authors: Shannon L. Taylor, Amaka J. Ibeh, Adam E Jakus, Ramille N Shah, David C Dunand
    Abstract:

    Abstract We present a novel additive manufacturing method for NiTi-Nb micro-trusses combining (i) extrusion-based 3D-printing of liquid inks containing NiTi and Nb powders, solvents, and a polymer binder into micro-trusses with 0/90° ABAB layers of parallel, ∼600 µm struts spaced 1 mm apart and (ii) subsequent heat-treatment to remove the binder and solvents, and then bond the NiTi powders using liquid phase Sintering via the formation of a Transient NiTi-Nb eutectic phase. We investigate the effects of Nb concentration (0, 1.5, 3.1, 6.7 at.% Nb) on the porosity, microstructure, and phase transformations of the printed NiTi-Nb micro-trusses. Micro-trusses with the highest Nb content exhibit long channels (from 3D-printing) and struts with smaller interconnected porosity (from partial Sintering), resulting in overall porosities of ∼75% and low compressive stiffnesses of 1–1.6 GPa, similar to those of trabecular bone and in agreement with analytical and finite element modeling predictions. Diffusion of Nb into the NiTi particles from the bond regions results in a Ni-rich composition as the Nb replaces Ti atoms, leading to decreased martensite/austenite transformation temperatures. Adult human mesenchymal stem cells seeded on these micro-trusses showed excellent viability, proliferation, and extracellular matrix deposition over 14 days in culture. Statement of Significance Near-equiatomic NiTi micro-trusses are attractive for biomedical applications such as stents, actuators, and bone implants because of their combination of biocompatibility, low compressive stiffness, high surface area, and shape-memory or superelasticity. Extrusion-based 3D-printing of NiTi powder-based inks into micro-trusses is feasible, but the subsequent Sintering of the powders into dense struts is unachievable due to low diffusivity, large particle size, and low packing density of the NiTi powders. We present a solution, whereby Nb powders are added to the NiTi inks, thus forming during Sintering a eutectic NiTi-Nb liquid phase which bonds the solid NiTi powders and improves densification of the struts. This study investigates the microstructure, porosity, phase transformation behavior, compressive stiffness, and cytocompatibility of these printed NiTi-Nb micro-trusses.

  • niti nb micro trusses fabricated via extrusion based 3d printing of powders and Transient liquid phase Sintering
    Acta Biomaterialia, 2018
    Co-Authors: Shannon L. Taylor, Amaka J. Ibeh, Adam E Jakus, Ramille N Shah, David C Dunand
    Abstract:

    Abstract We present a novel additive manufacturing method for NiTi-Nb micro-trusses combining (i) extrusion-based 3D-printing of liquid inks containing NiTi and Nb powders, solvents, and a polymer binder into micro-trusses with 0/90° ABAB layers of parallel, ∼600 µm struts spaced 1 mm apart and (ii) subsequent heat-treatment to remove the binder and solvents, and then bond the NiTi powders using liquid phase Sintering via the formation of a Transient NiTi-Nb eutectic phase. We investigate the effects of Nb concentration (0, 1.5, 3.1, 6.7 at.% Nb) on the porosity, microstructure, and phase transformations of the printed NiTi-Nb micro-trusses. Micro-trusses with the highest Nb content exhibit long channels (from 3D-printing) and struts with smaller interconnected porosity (from partial Sintering), resulting in overall porosities of ∼75% and low compressive stiffnesses of 1–1.6 GPa, similar to those of trabecular bone and in agreement with analytical and finite element modeling predictions. Diffusion of Nb into the NiTi particles from the bond regions results in a Ni-rich composition as the Nb replaces Ti atoms, leading to decreased martensite/austenite transformation temperatures. Adult human mesenchymal stem cells seeded on these micro-trusses showed excellent viability, proliferation, and extracellular matrix deposition over 14 days in culture. Statement of Significance Near-equiatomic NiTi micro-trusses are attractive for biomedical applications such as stents, actuators, and bone implants because of their combination of biocompatibility, low compressive stiffness, high surface area, and shape-memory or superelasticity. Extrusion-based 3D-printing of NiTi powder-based inks into micro-trusses is feasible, but the subsequent Sintering of the powders into dense struts is unachievable due to low diffusivity, large particle size, and low packing density of the NiTi powders. We present a solution, whereby Nb powders are added to the NiTi inks, thus forming during Sintering a eutectic NiTi-Nb liquid phase which bonds the solid NiTi powders and improves densification of the struts. This study investigates the microstructure, porosity, phase transformation behavior, compressive stiffness, and cytocompatibility of these printed NiTi-Nb micro-trusses.

Ramille N Shah - One of the best experts on this subject based on the ideXlab platform.

  • microstructure and porosity evolution during Sintering of ni mn ga wires printed from inks containing elemental powders
    Intermetallics, 2019
    Co-Authors: Shannon L. Taylor, Ramille N Shah, David C Dunand
    Abstract:

    Abstract Ni-29Mn-21.5Ga (at. %) wires are fabricated via a combination of (i) extrusion of liquid inks containing a binder, solvents, and elemental Ni, Mn, and Ga powders and (ii) heat treatments to remove the polymer binder and to interdiffuse and sinter the powders. To study the microstructural evolution, Sintering mechanisms, and grain growth in these wires, both ex situ metallography and in situ X-Ray tomography were conducted while Sintering at 800–1050 °C for up to 4 h. After debinding, Ga-rich regions melt and induce Transient liquid phase Sintering of the surrounding Ni and Mn powders, resulting in localized swelling of the wires and an increase in the wire porosity. After solidification of the melt and diffusion of the Ga into the Ni and Mn powders, solid-state Sintering occurs. The interdiffusion of Ni, Mn, and Ga during solid-state Sintering improves Sintering compared to fully pre-alloyed powders. At the end of the 4 h Sintering period, chemically homogenized, oligocrystalline wires with bamboo-like grains are observed with porosities ranging from 30 to 57%. Furthermore, significant grain growth occurs in wires sintered at 1000 and 1050 °C (11–35 μm vs. 1–10 μm initial powder size). The results from this study enable tailoring the porosity and grain size of printed Ni-Mn-Ga wires and 3D-printed micro-architectures and may be used to enhance their magnetic shape-memory and magnetocaloric effects in future work.

  • niti nb micro trusses fabricated via extrusion based 3d printing of powders and Transient liquid phase Sintering
    Acta Biomaterialia, 2018
    Co-Authors: Shannon L. Taylor, Amaka J. Ibeh, Adam E Jakus, Ramille N Shah, David C Dunand
    Abstract:

    Abstract We present a novel additive manufacturing method for NiTi-Nb micro-trusses combining (i) extrusion-based 3D-printing of liquid inks containing NiTi and Nb powders, solvents, and a polymer binder into micro-trusses with 0/90° ABAB layers of parallel, ∼600 µm struts spaced 1 mm apart and (ii) subsequent heat-treatment to remove the binder and solvents, and then bond the NiTi powders using liquid phase Sintering via the formation of a Transient NiTi-Nb eutectic phase. We investigate the effects of Nb concentration (0, 1.5, 3.1, 6.7 at.% Nb) on the porosity, microstructure, and phase transformations of the printed NiTi-Nb micro-trusses. Micro-trusses with the highest Nb content exhibit long channels (from 3D-printing) and struts with smaller interconnected porosity (from partial Sintering), resulting in overall porosities of ∼75% and low compressive stiffnesses of 1–1.6 GPa, similar to those of trabecular bone and in agreement with analytical and finite element modeling predictions. Diffusion of Nb into the NiTi particles from the bond regions results in a Ni-rich composition as the Nb replaces Ti atoms, leading to decreased martensite/austenite transformation temperatures. Adult human mesenchymal stem cells seeded on these micro-trusses showed excellent viability, proliferation, and extracellular matrix deposition over 14 days in culture. Statement of Significance Near-equiatomic NiTi micro-trusses are attractive for biomedical applications such as stents, actuators, and bone implants because of their combination of biocompatibility, low compressive stiffness, high surface area, and shape-memory or superelasticity. Extrusion-based 3D-printing of NiTi powder-based inks into micro-trusses is feasible, but the subsequent Sintering of the powders into dense struts is unachievable due to low diffusivity, large particle size, and low packing density of the NiTi powders. We present a solution, whereby Nb powders are added to the NiTi inks, thus forming during Sintering a eutectic NiTi-Nb liquid phase which bonds the solid NiTi powders and improves densification of the struts. This study investigates the microstructure, porosity, phase transformation behavior, compressive stiffness, and cytocompatibility of these printed NiTi-Nb micro-trusses.

  • niti nb micro trusses fabricated via extrusion based 3d printing of powders and Transient liquid phase Sintering
    Acta Biomaterialia, 2018
    Co-Authors: Shannon L. Taylor, Amaka J. Ibeh, Adam E Jakus, Ramille N Shah, David C Dunand
    Abstract:

    Abstract We present a novel additive manufacturing method for NiTi-Nb micro-trusses combining (i) extrusion-based 3D-printing of liquid inks containing NiTi and Nb powders, solvents, and a polymer binder into micro-trusses with 0/90° ABAB layers of parallel, ∼600 µm struts spaced 1 mm apart and (ii) subsequent heat-treatment to remove the binder and solvents, and then bond the NiTi powders using liquid phase Sintering via the formation of a Transient NiTi-Nb eutectic phase. We investigate the effects of Nb concentration (0, 1.5, 3.1, 6.7 at.% Nb) on the porosity, microstructure, and phase transformations of the printed NiTi-Nb micro-trusses. Micro-trusses with the highest Nb content exhibit long channels (from 3D-printing) and struts with smaller interconnected porosity (from partial Sintering), resulting in overall porosities of ∼75% and low compressive stiffnesses of 1–1.6 GPa, similar to those of trabecular bone and in agreement with analytical and finite element modeling predictions. Diffusion of Nb into the NiTi particles from the bond regions results in a Ni-rich composition as the Nb replaces Ti atoms, leading to decreased martensite/austenite transformation temperatures. Adult human mesenchymal stem cells seeded on these micro-trusses showed excellent viability, proliferation, and extracellular matrix deposition over 14 days in culture. Statement of Significance Near-equiatomic NiTi micro-trusses are attractive for biomedical applications such as stents, actuators, and bone implants because of their combination of biocompatibility, low compressive stiffness, high surface area, and shape-memory or superelasticity. Extrusion-based 3D-printing of NiTi powder-based inks into micro-trusses is feasible, but the subsequent Sintering of the powders into dense struts is unachievable due to low diffusivity, large particle size, and low packing density of the NiTi powders. We present a solution, whereby Nb powders are added to the NiTi inks, thus forming during Sintering a eutectic NiTi-Nb liquid phase which bonds the solid NiTi powders and improves densification of the struts. This study investigates the microstructure, porosity, phase transformation behavior, compressive stiffness, and cytocompatibility of these printed NiTi-Nb micro-trusses.

Amaka J. Ibeh - One of the best experts on this subject based on the ideXlab platform.

  • niti nb micro trusses fabricated via extrusion based 3d printing of powders and Transient liquid phase Sintering
    Acta Biomaterialia, 2018
    Co-Authors: Shannon L. Taylor, Amaka J. Ibeh, Adam E Jakus, Ramille N Shah, David C Dunand
    Abstract:

    Abstract We present a novel additive manufacturing method for NiTi-Nb micro-trusses combining (i) extrusion-based 3D-printing of liquid inks containing NiTi and Nb powders, solvents, and a polymer binder into micro-trusses with 0/90° ABAB layers of parallel, ∼600 µm struts spaced 1 mm apart and (ii) subsequent heat-treatment to remove the binder and solvents, and then bond the NiTi powders using liquid phase Sintering via the formation of a Transient NiTi-Nb eutectic phase. We investigate the effects of Nb concentration (0, 1.5, 3.1, 6.7 at.% Nb) on the porosity, microstructure, and phase transformations of the printed NiTi-Nb micro-trusses. Micro-trusses with the highest Nb content exhibit long channels (from 3D-printing) and struts with smaller interconnected porosity (from partial Sintering), resulting in overall porosities of ∼75% and low compressive stiffnesses of 1–1.6 GPa, similar to those of trabecular bone and in agreement with analytical and finite element modeling predictions. Diffusion of Nb into the NiTi particles from the bond regions results in a Ni-rich composition as the Nb replaces Ti atoms, leading to decreased martensite/austenite transformation temperatures. Adult human mesenchymal stem cells seeded on these micro-trusses showed excellent viability, proliferation, and extracellular matrix deposition over 14 days in culture. Statement of Significance Near-equiatomic NiTi micro-trusses are attractive for biomedical applications such as stents, actuators, and bone implants because of their combination of biocompatibility, low compressive stiffness, high surface area, and shape-memory or superelasticity. Extrusion-based 3D-printing of NiTi powder-based inks into micro-trusses is feasible, but the subsequent Sintering of the powders into dense struts is unachievable due to low diffusivity, large particle size, and low packing density of the NiTi powders. We present a solution, whereby Nb powders are added to the NiTi inks, thus forming during Sintering a eutectic NiTi-Nb liquid phase which bonds the solid NiTi powders and improves densification of the struts. This study investigates the microstructure, porosity, phase transformation behavior, compressive stiffness, and cytocompatibility of these printed NiTi-Nb micro-trusses.

  • niti nb micro trusses fabricated via extrusion based 3d printing of powders and Transient liquid phase Sintering
    Acta Biomaterialia, 2018
    Co-Authors: Shannon L. Taylor, Amaka J. Ibeh, Adam E Jakus, Ramille N Shah, David C Dunand
    Abstract:

    Abstract We present a novel additive manufacturing method for NiTi-Nb micro-trusses combining (i) extrusion-based 3D-printing of liquid inks containing NiTi and Nb powders, solvents, and a polymer binder into micro-trusses with 0/90° ABAB layers of parallel, ∼600 µm struts spaced 1 mm apart and (ii) subsequent heat-treatment to remove the binder and solvents, and then bond the NiTi powders using liquid phase Sintering via the formation of a Transient NiTi-Nb eutectic phase. We investigate the effects of Nb concentration (0, 1.5, 3.1, 6.7 at.% Nb) on the porosity, microstructure, and phase transformations of the printed NiTi-Nb micro-trusses. Micro-trusses with the highest Nb content exhibit long channels (from 3D-printing) and struts with smaller interconnected porosity (from partial Sintering), resulting in overall porosities of ∼75% and low compressive stiffnesses of 1–1.6 GPa, similar to those of trabecular bone and in agreement with analytical and finite element modeling predictions. Diffusion of Nb into the NiTi particles from the bond regions results in a Ni-rich composition as the Nb replaces Ti atoms, leading to decreased martensite/austenite transformation temperatures. Adult human mesenchymal stem cells seeded on these micro-trusses showed excellent viability, proliferation, and extracellular matrix deposition over 14 days in culture. Statement of Significance Near-equiatomic NiTi micro-trusses are attractive for biomedical applications such as stents, actuators, and bone implants because of their combination of biocompatibility, low compressive stiffness, high surface area, and shape-memory or superelasticity. Extrusion-based 3D-printing of NiTi powder-based inks into micro-trusses is feasible, but the subsequent Sintering of the powders into dense struts is unachievable due to low diffusivity, large particle size, and low packing density of the NiTi powders. We present a solution, whereby Nb powders are added to the NiTi inks, thus forming during Sintering a eutectic NiTi-Nb liquid phase which bonds the solid NiTi powders and improves densification of the struts. This study investigates the microstructure, porosity, phase transformation behavior, compressive stiffness, and cytocompatibility of these printed NiTi-Nb micro-trusses.

Adam E Jakus - One of the best experts on this subject based on the ideXlab platform.

  • niti nb micro trusses fabricated via extrusion based 3d printing of powders and Transient liquid phase Sintering
    Acta Biomaterialia, 2018
    Co-Authors: Shannon L. Taylor, Amaka J. Ibeh, Adam E Jakus, Ramille N Shah, David C Dunand
    Abstract:

    Abstract We present a novel additive manufacturing method for NiTi-Nb micro-trusses combining (i) extrusion-based 3D-printing of liquid inks containing NiTi and Nb powders, solvents, and a polymer binder into micro-trusses with 0/90° ABAB layers of parallel, ∼600 µm struts spaced 1 mm apart and (ii) subsequent heat-treatment to remove the binder and solvents, and then bond the NiTi powders using liquid phase Sintering via the formation of a Transient NiTi-Nb eutectic phase. We investigate the effects of Nb concentration (0, 1.5, 3.1, 6.7 at.% Nb) on the porosity, microstructure, and phase transformations of the printed NiTi-Nb micro-trusses. Micro-trusses with the highest Nb content exhibit long channels (from 3D-printing) and struts with smaller interconnected porosity (from partial Sintering), resulting in overall porosities of ∼75% and low compressive stiffnesses of 1–1.6 GPa, similar to those of trabecular bone and in agreement with analytical and finite element modeling predictions. Diffusion of Nb into the NiTi particles from the bond regions results in a Ni-rich composition as the Nb replaces Ti atoms, leading to decreased martensite/austenite transformation temperatures. Adult human mesenchymal stem cells seeded on these micro-trusses showed excellent viability, proliferation, and extracellular matrix deposition over 14 days in culture. Statement of Significance Near-equiatomic NiTi micro-trusses are attractive for biomedical applications such as stents, actuators, and bone implants because of their combination of biocompatibility, low compressive stiffness, high surface area, and shape-memory or superelasticity. Extrusion-based 3D-printing of NiTi powder-based inks into micro-trusses is feasible, but the subsequent Sintering of the powders into dense struts is unachievable due to low diffusivity, large particle size, and low packing density of the NiTi powders. We present a solution, whereby Nb powders are added to the NiTi inks, thus forming during Sintering a eutectic NiTi-Nb liquid phase which bonds the solid NiTi powders and improves densification of the struts. This study investigates the microstructure, porosity, phase transformation behavior, compressive stiffness, and cytocompatibility of these printed NiTi-Nb micro-trusses.

  • niti nb micro trusses fabricated via extrusion based 3d printing of powders and Transient liquid phase Sintering
    Acta Biomaterialia, 2018
    Co-Authors: Shannon L. Taylor, Amaka J. Ibeh, Adam E Jakus, Ramille N Shah, David C Dunand
    Abstract:

    Abstract We present a novel additive manufacturing method for NiTi-Nb micro-trusses combining (i) extrusion-based 3D-printing of liquid inks containing NiTi and Nb powders, solvents, and a polymer binder into micro-trusses with 0/90° ABAB layers of parallel, ∼600 µm struts spaced 1 mm apart and (ii) subsequent heat-treatment to remove the binder and solvents, and then bond the NiTi powders using liquid phase Sintering via the formation of a Transient NiTi-Nb eutectic phase. We investigate the effects of Nb concentration (0, 1.5, 3.1, 6.7 at.% Nb) on the porosity, microstructure, and phase transformations of the printed NiTi-Nb micro-trusses. Micro-trusses with the highest Nb content exhibit long channels (from 3D-printing) and struts with smaller interconnected porosity (from partial Sintering), resulting in overall porosities of ∼75% and low compressive stiffnesses of 1–1.6 GPa, similar to those of trabecular bone and in agreement with analytical and finite element modeling predictions. Diffusion of Nb into the NiTi particles from the bond regions results in a Ni-rich composition as the Nb replaces Ti atoms, leading to decreased martensite/austenite transformation temperatures. Adult human mesenchymal stem cells seeded on these micro-trusses showed excellent viability, proliferation, and extracellular matrix deposition over 14 days in culture. Statement of Significance Near-equiatomic NiTi micro-trusses are attractive for biomedical applications such as stents, actuators, and bone implants because of their combination of biocompatibility, low compressive stiffness, high surface area, and shape-memory or superelasticity. Extrusion-based 3D-printing of NiTi powder-based inks into micro-trusses is feasible, but the subsequent Sintering of the powders into dense struts is unachievable due to low diffusivity, large particle size, and low packing density of the NiTi powders. We present a solution, whereby Nb powders are added to the NiTi inks, thus forming during Sintering a eutectic NiTi-Nb liquid phase which bonds the solid NiTi powders and improves densification of the struts. This study investigates the microstructure, porosity, phase transformation behavior, compressive stiffness, and cytocompatibility of these printed NiTi-Nb micro-trusses.